Plant-based cellulose boosts eco-friendly plywood adhesive performance
Researchers have developed a way to strengthen plywood adhesives by adding micro-fibrillated cellulose to lignin-based formulations, reducing reliance on petroleum-derived chemicals. The finding could help plywood manufacturers lower costs and environmental impact while maintaining structural quality.
Originaltitel: Micro-Fibrillated Cellulose in Lignin–Phenol–Formaldehyde Adhesives for Plywood Production
<p>Petrochemical-based phenol–formaldehyde (PF) adhesives are widely used in plywood production. To substitute phenol in the synthesis of PF adhesives, lignin can be added due to its structural similarity to phenol. Moreover, micro-fibrillated cellulose (MFC) can further enhance the bond performance, mechanical properties, and toughness of adhesive systems. Thus, the aim of this study was to evaluate the adhesion performance of lignin–PF (LPF) adhesives reinforced with MFC. In LPF formulations, three levels of MFC (0, 15, and 30 wt% based on the total solid content of adhesives) were added to the homogenous adhesive mixture. Three-layer plywood panels from birch (<em>Betula pendula</em> Roth.) veneers were assembled after hot pressing at 130 °C under two pressing durations, e.g., 60 and 75 s/mm. Tensile shear strength was measured at dry (20 °C and 65% RH) and wet conditions (water soaked at room temperature for 24 h). The results indicated that the addition of lignin reduced the strength of LPF adhesives in both dry and wet conditions compared to the control PF adhesive. However, MFC reinforcement enhanced the shear strength properties of the plywood. Furthermore, a longer pressing time of 75 s/mm slightly increased the shear strength.</p>